Please be aware that this product can only be shipped to the following countries: Austria, Germany, Switzerland, Belgium, Bulgaria, Croatia, Czech Republic, Denmark, France, Greece, Hungary, Italy, Luxembourg, Netherlands, Norway, Poland, Portugal, Romania, Serbia,  Slovakia, Slovenia, Spain, and the United Kingdom!

• Free from nonylphenol and DETA
• Low viscosity, solvent- and filler-free
• Fast impregnation of glass, aramid and carbon fibres
• High static and dynamic strength
• Low surface tension, good adhesion and low curing shrinkage
• Ideal for bonding wood, metal, Styrofoam®, etc.

Epoxy resin L with the corresponding hardeners is the most frequently used laminating and bonding resin from the R&G product range.

Epoxy resin L with Hardener L has similar mechanical properties to the laminating systems commonly used in aircraft construction.

• Processing time: 40 minutes (100 g / 20 °C)
• Curing time (at 23 °C): 24 hours, warm curing optional
• Heat distortion temperature: approx. 70 °C, up to a maximum of 80 °C with an additional 15 hours at 60 °C

Mixing ratio:

• 100 : 40 parts by weight epoxy resin L : hardener L
• 100 : 45 parts by volume epoxy resin L : hardener L

Processing:
It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as pressing and winding.