Please be aware that this product can only be shipped to the following countries: Austria, Germany, Switzerland, France, Italy, Belgium, Bulgaria, Denmark, Great Britain, Croatia, Luxembourg, Netherlands, Poland, Romania, Sweden, Slovakia, Slovenia, Czech Republic, HungaryPlease note that shipping this item to Finland is not possible!

Hardener for Epoxy Resin L
The well-proven R&G Epoxy Resin L in combination with Hardener GL 1 offers an approval by the Germanische Lloyd for the construction of boats and rotor blades for wind turbines.

Mixing ratio:
100 : 30 parts by weight resin : hardener
100 : 35 parts by volume resin : hardener

Processing time: approx. 30 minutes

Properties:
  • Low viscosity (820 mPas at 25 °C)
  • Fully cures at 10 °C
  • Glass transition temperature (Tg) > 80 °C (post-curing at 70 °C / 15 h)
  • Ambient curing does not result in brittleness (at 20 °C)
  • High static and dynamic strength

This newly delevoped resin system is ideal for wetting-out glass, aramid and carbon fibres. It exhibits a very good price/performance ratio and is suitable for the following processing procedures:
  • Resin infusion (RI)
  • RTM (resin transfer moulding)
  • Press moulding
  • Vacuum moulding
  • Filament winding
  • Hand laminating

The resin component itself is absolutely free of crystallization due to its Bisphenol A/F base! The resin system is ambient curing and develops no distinctive brittleness even at curing temperatures below 20 °C. We however recommend, to improve the physical and chemical properties, to perform a post-curing at least at 40 °C over 15 h.

Mixing table with processing times of Epoxy Resin L + mixed Hardeners GL 1/2.
The mixing ratio of 100: 30 resin to hardener remains unchanged.

Please order Epoxy Resin L order no. 100135-X separately


Technical data

Menge 0,75 kg
Ausreichend für 2,5 kg Epoxydharz L