Please be aware that this product can only be shipped to the following countries: Austria, Germany, Switzerland, Belgium, Bulgaria, Croatia, Czech Republic, Denmark, France, Greece, Hungary, Italy, Luxembourg, Netherlands, Norway, Poland, Portugal, Romania, Serbia,  Slovakia, Slovenia, Spain, and the United Kingdom!

Epoxy Resin L + Hardener S (15 min)

• Free from nonylphenol, benzyl alcohol and DETA
• Low viscosity, solvent- and filler-free
• Fast impregnation of glass, aramid and carbon fibres
• High static and dynamic strength
• Low surface tension, good adhesion and low curing shrinkage
• Ideal for bonding wood, metal, Styropor® etc.

Epoxy resin L with the corresponding hardeners is the most frequently used laminating and bonding resin from the R&G product range.

Epoxy resin L with Hardener S has similar mechanical properties to the laminating systems commonly used in aircraft construction.

Mixing ratio:
100 : 40 parts by weight Epoxy Resin L : Hardener S
100 : 45 parts by volume Epoxy Resin L : Hardener S

• Curing time (at 23 °C): 16 - 24 hours
• Cold hardening, hardens from 5 °C (low temperature hardener)
• Heat distortion temperature: Approx. 65 °C
• Processing time: 15 minutes (100 g / 20 °C)

Processing:
It can be processed in all common processes such as hand lamination, pressure and vacuum impregnation as well as pressing and winding.

CYTOX expert opinion on the Resin System Epoxy Resin L + Hardener S (see below under additional information): this system is not cytotoxic (cell-damaging), important for applications in medical technology.